1.
EFFECT OF CeO2 ON THE STRUCTURE AND PROPERTIES OF ALUMINA-ZIRCONIA CERAMICS PREPARED BY PRESSURELESS SINTERING AND HOT PRESSING
-
(Not-set)
-
The influence of ceria (CeO2: 0…3,56 wt. %) and sintering method (pressureless sintering in air, hot pressing in Ar) on the phase composition, microstructure, and properties of alumina-zirconia ceramics ...
-
2.
SYNTHESIS OF MARBLITE IN A PLASMA GLASS FURNACE
-
(Not-set)
-
The possibility of using waste from the enrichment of ferruginous quartzites of KMA and waste from vanadium production for the plasma synthesis of marblite and structural elements of a plasma glass furnace ...
-
3.
THE POSSIBILITY OF USING WASTE FROM THE ENRICHMENT OF FERRUGINOUS QUARTZITE KMA IN THE PRODUCTION OF CERAMIC BUILDING MATERIALS
-
(Not-set)
-
The possibility of using waste from the enrichment of ferruginous quartzites of KMA is considered. The chemical composition of waste from Lebedinsky GOK has been investigated. It has been established that ...
-
4.
FACING BUILDING MATERIAL BASED ON CULLET MODIFIED WITH POTASSIUM HYDROXIDE
-
(Not-set)
-
The technology of facing material based on mechanically activated cullet modified with potassium hydroxides has been developed. The phase composition, macro- and microstructure of the lining material are ...
-
5.
ENVIRONMENTAL ASPECTS OF THE USE OF BATTLE GLASS FOR THE PRODUCTION OF GLASS CONCRETE
-
(Not-set)
-
The technology of glass concrete based on dispersed container and sheet glass has been developed. It is shown that when Portland cement and cullet are ground together, when a specific surface area of 5890 ...
-
6.
FACING BUILDING MATERIAL BASED ON MECHANICALLY ACTIVATED CULLET MODIFIED WITH SODIUM HYDROXIDE
-
(Not-set)
-
The technology of facing material based on mechanically activated cullet modified with sodium hydroxides has been developed. The phase composition, macro- and microstructure of the lining material are ...
-
7.
MODERN TRENDS IN THE DEVELOPMENT OF TECHNOLOGIES FOR MATTING GLASS PRODUCTS
-
(Not-set)
-
Modern trends in the development of technologies for matting glass and glass products are considered. An effective technology of glass matting using alternative energy sources, in particular low-temperature ...
-
8.
THE POSSIBILITY OF USING VANADIUM WASTE IN THE TECHNOLOGY OF WALL CERAMICS
-
(Not-set)
-
A complex of physico-chemical studies was carried out: X-ray phase analysis, differential thermal analysis, chemical analysis of vanadium production waste. It has been established that these wastes containing ...
-
9.
Plasma Technology for the Production of Glass
Pellets Based on Waste from the Enrichment of Ferruginous Quartzite KMA
-
(Not-set)
-
A technology has been developed for producing glass microspheres in a plasma reactor based on the wastes of enrichment of ferruginous quartzites KMA. The regularities of the influence of the flow rate ...
-
10.
Zirconia/Alumina Ceramic Composites Containing Strontium Hex-aaluminate
-
(Not-set)
-
The preparation and mechanical properties of composites 20 & # 37; molar fraction of Al 2 O 3 and 80 & # 37; [3Yb & # 8211; TZP] modified with strontium oxide. It is shown that in the process of heat ...
-
11.
Use of improved glassy phosphate composition for water treatment
-
(At the enterprises and institutes)
-
The results of experiments on studying the properties of a glassy phosphate composition, modernized with copper-containing additives, are presented. The composition is designed to protect the surfaces ...
-
12.
Changes in phase composition and strength of Al2O3-ZrO2 ce-ramics after hydrothermal ageing
-
(Biomaterials)
-
The influence of the mass content of Al 2 O 3 on the stability of the phase composition and the strength of the ceramics of the Al 2 O 3 -3Y system has been determined. -ZrO 2 prepared according ...
-
13.
Calcium phosphate powder synthesis from calcium formiate and ammonium hydro-phosphate for bio-compatible resorbable bi-phase ceramics production
-
(Biomaterials)
-
Calcium phosphate powder was synthesized from calcium formate Ca (CHO 2 ) 2 and ammonium hydrogen phosphate (NH 4 ) 2 HPO 4 at the Ca / P ratio in the initial aqueous solutions equal to 1. The ...
-
14.
Technological regime of melting Pb-containing glass
-
(Science for glass production)
-
The issues of mathematical modeling of the process of melting lead-containing glasses used in the production of ceramic paints are considered. On the basis of laboratory studies, the stages of physicochemical ...