Powders of hydroxyapatite (HA) Ca10(PO4)6(OH)2 treated in 0.25M aqueous solutions of ammonium NH4H2PO4, sodium NaH2PO4 and potassium KH2PO4 dihydrophosphates for 1 hour under stirring were used for ceramics ...
Obtaining new ceramic and composite materials is associated with a number of difficulties, the key of which is the lack of pure initial refractory components. The presence of impurities in the powders ...
The possibility of obtaining ceramic fibers of zirconium oxide by electrospinning is considered. The factors influencing the fiber diameter and the presence of tape inclusions have been established. It ...
Ceramics in the Ca 2 P 2 O 7 -Ca (PO 3 ) 2 was obtained by firing a cement stone made from a powder mixture containing ?-tricalcium phosphate ?-Ca 3 (PO 4 ) 2 and monocalcium phosphate monohydrate ...
The structure and phase composition of lanthanum hexaboride ceramic material samples prepared by sintering are investigated. It was found that the formation of a high-quality consolidated structure with ...
Investigations of changes in the phase composition and structure of modern ceramic materials under the action of a high-intensity light flux have been carried out. For the experiment, the technological ...
A sol-gel process for producing aluminum-magnesium spinel fibers from a fiber-forming precursor based on aluminum and magnesium polycarboxylates is considered. The principal possibility of obtaining discrete ...
The creation of reaction-cured coatings is a promising direction in the field of protection of metallic and non-metallic structural materials during operation in aviation technology. The main feature of ...
A 3D matrix was obtained based on a sintered composite material made of bioactive glass and dicalcium phosphate dihydrate. The regularities of the influence of the ratio of the mixture components and the ...
The description of the information system containing reference information on the physicochemical, biological properties of orthophosphates, pyrophosphates and ultraphosphates of calcium is given. In addition ...
A number of composite materials based on dicalcium phosphate dihydrate and bioactive glass 50S25N5P with physiologically safe pH values ??and compressive strength from 4 to 22 MPa have been developed. ...
The results of a two-stage synthesis of tricalcium phosphate by the wet method followed by high-temperature treatment are presented. The influence of the introduction of tricalcium silicate and alkaline ...