It is shown that the introduction of ferroelectric additives into glass enamel coatings is promising in order to improve their dielectric characteristics. The limits of the added additive for low alkaline borosilicate enamel are determined. A comparative table of the properties of the original and composite enamels is given. The dielectric properties of the new material have been determined and the absence of dissolution of the additive in the glass enamel has been established. Tab. 1, ill. 5, bibliography: 7 titles.
Silkin E. Synthesis of ozone in electrical discharges and increasing its efficiency. Part 1 // Components and technologies. 2008. N 6. P. 136 - 143.
Samoilovich VT, Gibalov VI, Kozlov KV Physical chemistry of a barrier discharge. Moscow: Moscow State University Publishing House, 1989.176 p.
Gorzkowski EP, Pan M.-J., Bender BC, Wu CM Glass - ceramics of barium strontium titanate for high energy density capacitors // Journal of Electroceramics. 2007. N3-4. P.269- 276.
Gavrilyuk VB Ozone synthesis in high-frequency ozonizers with various dielectric coatings: dis. Cand. chem. sciences. M., 1988.
Shabrova EB Influence of properties and composition of glass-crystalline and glass-enamel coatings of electrodes on the electrosynthesis of ozone in a barrier discharge: dis. Cand. tech. sciences. M., 2000.
Ik Jin Choi, Yong Soo Cho. Effects of various oxide filler on physical and dielectric properties of calcium alumoborosilicate-based dielectrics // Journal of Electroceramics. 2009. N2-4. P. 185 - 190.
Ferroelectrics and antiferroelectrics / TA Smolenskiy, VA Bokov, NN Krainik [and others]. L .: Nauka, 1971.476 p.
The article can be purchased
electronic!
PDF format
Not on sale
UDK 666.293.52:537.226.2
Article type:
Coatings. Enamels.
Make a request