The chemical-mineralogical compositions, new formations of crystalline phases of minerals and the main properties of the ceramic mass were studied using iron-containing dust from the gas cleaning of steel-smelting furnaces of metallurgical production during sintering in the temperature range of 950 – 1100 ?C. It has been established that with the introduction of gas cleaning dust, the structure is stabilized and the sintering temperature of the ceramic shard is reduced.
Saidamir S. Tairov – senior researcher, lab. “Chemistry and chemical technology of silicates”, Institute of general and inorganic chemistry, Academy of sciences of the Republic of Uzbekistan. E-mail: This email address is being protected from spambots. You need JavaScript enabled to view it..
Zulayho R. Kadyrova – doctor of chemical sciences, professor, head of lab. “Chemistry and chemical technology of silicates” Institute of general and Inorganic Chemistry, Academy of sciences of the Republic of Uzbekistan. E-mail: This email address is being protected from spambots. You need JavaScript enabled to view it..
Khikmatula L. Usmanov – candidate of technical sciences, Senior Researcher, Lab. “Chemistry and Chemical Technology of silicates”, Institute of general and inorganic chemistry, Academy of Sciences of the Republic of Uzbekistan. E-mail: This email address is being protected from spambots. You need JavaScript enabled to view it..
1. Абдрахимов В. З. Фазовые превращения при обжиге керамических плиток на основе отходов обогащения // Стекло и керамика. 1992. № 3. С. 23 – 25.[Abdrakhimov V. Z. Phase transformations occurring during the firing process of ceramic tiles based on beneficiation tailings // Glass Ceram. 1992. V. 49, No. 3. P. 140 – 144.]
2. Миненкова Г. Я., Дятлова Е. М., Михальская Т. И. Керамические облицовочные плитки на основе местного сырья и отходов промышленности // Ресурсосберегающие и экологически чистые технологии: тр. науч.-техн. конф. Гродно, 1995. Ч. 1. С. 220 – 225.
3. Абдрахимов В. З. Фазовый состав облицовочных плиток на основе отходов производств // Стекло и керамика. 1990. № 9. С. 21 – 23.[Abdrakhimov V. Z. Phase composition of facing tiles based on production scrap // Glass Ceram. 1990. V. 47, No. 9. P. 361 – 363.]
4. Салахов А. М. Современные керамические материалы: учеб. пособие. Казань: КФУ, 2016. 410 с.
5. Апенская Д. Е., Сухих П. Н., Карпюк Л. Ю. и др. Расширение сырьевой базы производства эффективных керамических строительных материалов // Фундаментальные исследования. 2018. № 12. С. 197 – 202.
6. Никифорова Э. М., Еромасов Р. Г., Васильева М. Н. и др. Фазовые превращения в системах: полиминеральное глинистое сырье – примеси – минерализатор // Современные проблемы науки и образования: электрон. науч. журнал. 2012. № 3. Дата публикации: 14.05.2012. Раздел Технические науки.
7. Сабиров Б. Т., Кадырова З. Р., Таиров С. С. Разработка оптимальных составов керамических плиток с использованием барханных песков // Стекло и керамика. 2018. № 9. С. 36 – 39.[Sabirov B. T., Kadyrova Z. R., Tairov S. S. Development of Optimal Compositions of Ceramic Tiles Using Dune Sand // Glass Ceram. 2019. V. 75, No. 9-10. P. 363 – 365.]
8. Kadyrova Z. R., Purkhanatdinov A. P., Niyazova Sh. M. Study of Karakalpakstan Bentonite Clay for Producing Ceramic Heat-Insulating // Materials Refractories and Industrial Ceramics. 2021. V. 61. P. 478 – 480.
9. Ниязова Ш. М., Кадырова З. Р., Усманов Х. Л. и др. Физико-химические свойства минеральных волокон, полученных на основе андезибазальтов // Стекло и керамика. 2022. № 3. С. 38 – 45.[Niyazova Sh. M., Kadyrova Z. R., Usmanov Kh. L., et al. Physicochemical properties of andesitic basalt mineral fibers // Glass Ceram. 2022. V.79, No. 3-4. Р. 107 – 111.]
10. Ниязова Ш. М., Кадырова З. Р., Усманов Х. Л., Хомидов Ф. Г. Химико-минералогические исследования магматических пород Узбекистана для получения теплоизоляционных материалов // Стекло и керамика. 2018. № 12. С. 40 – 44.[Niyazova Sh. M., Kadyrova Z. R., Usmanov Kh. L., Khomidov F. G. Сhemical and Mineralogical Studies of Magmatic Rocks of Uzbekistan for Obtaining Heat-Insulating Materials // Glass Ceram. 2019. V. 75, No. 11-12. P. 491 – 495.]
11. ГОСТ 13996–2019. Плитки керамические. Общие технические условия. Дата введения 2020-06-01. М.: Стандартинформ, 2019.
12. О’zDSТ 823–97. Плитки керамические глазурованные для внутренней облицовки стен. Технические условия ?? Glazed ceramic tiles for interior wall coverings. Technical specifications. Дата вступления в силу 19.09.1997.
13. Толкачев С. С. Таблицы межплоскостных расстояний. Л.: Химия, 1968. 132 с.
14. X-Ray ASTM Standards. Pt 17. Refractories, Glass, Ceramic Materials, Carbon and Graphite Products. Philadelphia: ASTM, 2005. Р. 7 – 9, 51 – 61.
15. Мелешко В. Ю., Махленкова Л. Н. Использование белорусских месторождений необогащенных каолинов в производстве керамических изделий // Строительные материалы. 2010. № 1. С. 41 – 43.
16. Пат. RU 2463275. Влияние природы алюминийсодержащего соединения и механической активации смесей с каолином на синтез муллита / Е. Г. Аввакумов, Г. Г. Лепезин, Ю. В. Сереткин, О. Б. Винокурова. Опубл. 10.10.2012.
17. Вакалова Т. В., Хабас Т. А., Рева И. Б. Практикум по основам технологии тугоплавких неметаллических и силикатных материалов. Томск: Изд-во Томск. ПУ, 2013. 176 с.
18. Дятлова Е. М., Бирюк В. А. Химическая технология керамики и огнеупоров: Лабораторный практикум. Минск: БГТУ, 2006. 284 с.
The article can be purchased
electronic!
PDF format
500
DOI: 10.14489/glc.2023.01.pp.041-046
Article type:
Research Article
Make a request