Laboratory samples of reaction-sintered silicon carbide ceramics with permanent adhesive joints were obtained based on isopropyl alcohol and phenol-formaldehyde resin solutions with different contents of carbide and carbon particles. The joints have the following key structural physical and mechanical characteristics depending on the ratio of the phase components formed in the volumetric joining zone: thickness of the silicon layer in the seam is 20…130 ?m, flexural strength is 40…250 MPa, longitudinal sound velocity is 10 750…11 300 m/s, density is 3.07…3.08 g/cm3. It was experimentally established that varying the content of silicon carbide particles in the adhesive suspension from 20 to 80 % by weight makes it possible to achieve 30…75 % of the strength of the base material of the reaction-sintered silicon carbide ceramics.
Mikhail A. Markov – Doctor of Technical Sciences, head of the Laboratory “Technical Ceramics”, National Research Center “Kurchatov Institute” – Central Research Institute of Structural Materials “Prometey”, St. Petersburg, Russia
Andrey G. Chekuryaev – engineer of the 2rd category, National Research Center “Kurchatov Institute” – Central Research Institute of Structural Materials “Prometey”, St. Petersburg, Russia
Anton N. Belyakov – senior research fellow, National Research Center “Kurchatov Institute” – Central Research Institute of Structural Materials “Prometey”, St. Petersburg, Russia
Daria A. Dyuskina – engineer of the 2rd category, National Research Center “Kurchatov Institute” – Central Research Institute of Structural Materials “Prometey”, St. Petersburg, Russia; Saint-Petersburg State Institute of Technology, St. Petersburg, Russia
Alexander D. Kashtanov – Doctor of Technical Sciences, advisor to the general director, National Research Center “Kurchatov Institute” – Central Research Institute of Structural Materials “Prometey”, St. Petersburg, Russia
Alexander N. Nikolaev – leading engineer, National Research Center “Kurchatov Institute” – Central Research Institute of Structural Materials “Prometey”, St. Petersburg, Russia
Alina D. Bykova – senior research fellow, National Research Center “Kurchatov Institute” – Central Research Institute of Structural Materials “Prometey”, St. Petersburg, Russia
1. Ruys A. J. Silicon carbide ceramics structure, properties, and manufacturing. Elsevier, 2023. 586 p.
2. Riedel R. Handbook of ceramic hard materials. 1st ed. Weinheim: Wiley–VCH, 2000. V. 2. P. 683 – 748.
3. Briggs J. Engineering ceramics in Europe and the USA. Enceram. Menith Wood. UK, Worcester, 2011. 331 р.
4. Markov M. A., Krasikov A. V., Kravchenko I. N., et al. Development of novel ceramic construction materials based on silicon carbide for products of complex geometry // Journal of Machinery Manufacture and Reliability. 2021. V. 50, No. 2. P. 158 – 163.
5. Chin H., Cheong K., Ismail A. A Review on die attach materials for SiC-based high-temperature power devices // Metallurgical and Materials Transactions B. 2010. V. 41. P. 824 – 832.
6. Гаршин А. П., Гропянов В. М., Зайцев Г. П. и др. Керамика для машиностроения. М.: Научтехлитиздат, 2003. 384 с.
7. Morrell R. Handbook of properties of technical and engineering ceramics. Hmso: London, UK, 1987. 348 p.
8. Гнесин Г. Г. Бескислородные керамические материалы. Киев: Техника, 1987. 152 с.
9. Belyakov A. N., Markov M. A., Kravchenko I. N., et al.Contemporary materials and their application in the construction of special engineering high-temperature objects // Refractories and Industrial Ceramics. 2023. V. 64, No. 3. P. 256 – 264.
10. Гнесин Г. Г. Карбидокремниевые материалы. М.: Металлургия, 1977. 216 с.
11. Гаршин А. П. Карбид кремния. Монокристаллы, порошки и изделия на их основе. Санкт-Петербург: Изд-во Политехнического ун-та, 2006. 124 с.
12. Kriegesmann J. Processing of silicon carbide-based ceramics // Comprehensive Hard Materials. 2014. P. 89 – 175.
13. Belyakov A. N., Markov M. A., Dyuskina D. A., et al. A comparative study of methods for obtaining silicon carbide ceramic materials // Refractories and Industrial Ceramics. 2023. V. 64, No. 3. P. 299 – 310.
14. Izhevskyi V. A., Genova L. A., Bressiani J. C., et al. Review article: Silicon carbide. structure, propertyes and processing // Ceramica. 2000. V. 46(297). P. 4 – 13.
15. Scafe E., Giunta G., Fabbri L., et al. Mechanical behavior of silicon-silicon carbide composites // Journal of the European Ceramic Society. 1996. V. 16, No. 7. P. 703 – 713.
16. Sangsuwan P., Orejas J. A., Gatica J. E., et al. Reaction-bonded silicon carbide by reactive infiltration // Industrial & Engineering Chemistry Research. 2001. V. 40, No. 23. P. 5191 – 5198.
17. Самойлов В. М., Породзинский И. А. Получение и исследование карбидкремниевых материалов на основе реакционносвязанного карбида кремния // Перспективные материалы. 2014. № 3. С. 67 – 71.
18. Параносенков В. П., Чикина А. А., Андреев М. А. Конструкционные материалы на основе самосвязанного карбида кремния // Огнеупоры и техническая керамика. 2006. № 7. С. 37 – 40.
19. Гаршин А. П., Чулкин С. Г. Реакционно-спеченные карбидокремниевые материалы конструкционного назначения. Физико-механические и триботехнические свойства. Санкт-Петербург: Изд-во Политехнического ун-та, 2006. 83 с.
20. Дьячкова Л. Н., Звонарев Е. В., Шелехина В. М. и др. К вопросу о получении карбидокремниевых материалов методом реакционного спекания // Инженерно-физический журнал. 1997. Т. 70, № 2. С. 260 – 263.
21. Lu Zh., Ziong L., Gao J., et al. Microstructure, porosity and resistivity in reaction-bonded silicon carbide // Xi'an jiaotong daxue xuebao. 1999. V. 33, No. 4. P. 48 – 51.
22. Ness J. N., Page T. F. Microstructural evolution in reaction-bonded silicon carbide // Journal of Materials Science. 1986. V. 21, No. 4. P. 1377 – 1397.
23. Huang Q.-W., Zhu L.-H. High-temperature strength and toughness behaviors for reaction-bonded SiC ceramics below 1400 °C // Mater. Lett. 2005. V. 59, No. 14–15. P. 1732 – 1735.
24. Belyakov A. N., Markov M. A., Kravchenko I. N., et al. Structural and physicomechanical properties of silicon carbide-based reaction-sintered ceramics // Russian Metallurgy (Metally). 2024. V. 2024, No. 7. P. 1536 – 1543.
25. Markov M. A., Vikhman S. N., Belyakov A. N., et al. High-temperature bending tests of reaction-sintered silicon carbide-based ceramic materials // Russian Journal of Applied Chemistry. 2023. V. 96, No. 1. P. 16 – 20.
26. Belyakov A. N., Markov M. A., Chekuryaev A. N., et al. Investigation of the reaction-sintered B4C–SiC materials produced by hot slip casting // Glass Physics and Chemistry. 2023. V. 49, No. 3. P. 306 – 313.
27. Перевислов С. Н., Чупов В. Д. Реакционно-спеченные композиционные материалы на основе нитрида и карбида кремния // Вопросы материаловедения. 2013. № 2(74). С. 45 – 52.
28. Nesmelov D. D., Perevislov S. N. Science for ceramic production: Reaction sintered materials based on boron carbide and silicon carbide (Review) // Glass and Ceramics. 2015. V. 71, No. 9–10. P. 313 – 319. DOI: 10.1007/s10717-015-9677-7
29. Suyama S., Kameda T., Itoh Y. Development of high-strength reaction-sintered silicon carbide // Diamond and Related Materials. 2003. V. 12, No. 3 – 7. P. 1201 – 1204. DOI: 10.1016/S0925-9635(03)00066-9
30. Perevislov S. N. Determination of the temperature coefficient of linear expansion of materials based on silicon carbide // Refractories and Industrial Ceramics. 2021. V. 61, No. 6. P. 665 – 670. DOI: 10.1007/s11148-021-00539-y
31. ГОСТ 24409–80. Материалы керамические электротехнические. Методы испытаний. М.: Изд-во стандартов, 1982, 30 с.
32. ГОСТ 25961–83. Инструмент абразивный. Акустический метод контроля физико-механических свойств. М.: Изд-во стандартов, 1984, 29 с.
The article can be purchased
electronic!
PDF format
700 руб
DOI: 10.14489/glc.2026.01.pp.021-030
Article type:
Research Article
Make a request